Light

Scientific Reports volume 13, Article number: 13886 (2023) Cite this article

130 Accesses

1 Altmetric

Metrics details

Toxic dyes in water bodies and bacterial pathogens pose serious global challenges to human health and the environment. Zinc oxide nanoparticles (ZnO NPs) demonstrate remarkable photocatalytic and antibacterial potency against reactive dyes and bacterial strains. In this work, PVP-ZnO NPs have been prepared via the co-precipitation method using polyvinylpyrrolidone (PVP) as a surfactant. The NPs’ microstructure and morphology were studied using X-ray diffraction (XRD), having a size of 22.13 nm. High-resolution transmission electron microscope (HR-TEM) and field emission scanning electron microscopy (FESEM) analysis showed spherical-shaped PVP-ZnO NPs with sizer ranging from 20 to 30 nm. Fourier Transform Infrared Spectroscopy (FT-IR) confirmed the hybrid nature of the NPs, and UV–Vis spectroscopy showed an absorption peak at 367 nm. The PVP-ZnO NPs exhibited high photocatalytic activity, achieving 88% and nearly 95% degradation of reactive red-141 azo dye with 10 mg and 20 mg catalyst dosages, respectively. The antibacterial properties of the NPs were demonstrated against Escherichia coli and Bacillus subtilis, with inhibition zones of 24 mm and 20 mm, respectively. These findings suggest that PVP-ZnO NPs can be effectively used for water treatment, targeting both dye and pathogenic contaminants.

The textile industry has recently drawn much attention due to numerous dyes posing poisonous and cancer-causing endangering effects on all tropical species. Additionally, the dyes containing waste products from other businesses that produce food, process leather, make paper, print, use paints, and cosmetics pose serious environmental hazards due to their leakage into freshwaters. Among all the dye effluents, azo dyes are the most popular and are quite dangerous. They are complex aromatic molecules, and in general, the structure of the dye is stable1,2,3,4. Because their limited degradability and incomplete degradation of the dye led to numerous toxic compounds, hence are resistant to wastewater handling techniques8. Among the various azo dyes, reactive red-141 azo dye is widely used in textile industries and has been reported as the most dangerous to the environment and human health. Therefore, the immediate removal of these dyes from natural water sources has become important.

Adsorption, membrane separation, physical and chemical coagulation, advanced oxidation processes (AOPs), and biodegradation are some methods reported for wastewater treatment5. However, due to the advantages of minimal energy input, simple operation, cleanness, and efficiency, semiconductor photocatalysis technology has been widely used to degrade pollutants and decompose water to produce hydrogen6,7. Photocatalytic oxidation has garnered significant attention in environmental protection research, primarily for its utility in the photodegradation of organic pollutants. This technology boosts several notable advantages, including cost-effectiveness in terms of operational expenses, exceptional efficacy in removing intricate chemical compounds, absence of reliance on supplementary materials, harnessing of freely available solar energy, and the ability to execute the process under ambient temperature and pressure conditions. Extensive research efforts have led to the development and utilization of numerous nanomaterials fabricated from semiconducting oxides and sulphides, effectively applied in the photocatalytic application8,9.

Moreover, the emergence of bacterial pathogens in water bodies is also a worldwide issue. Recently, bacterial pathogens have been consistently identified in wastewater treatment plants, suggesting that these plants serve as significant reservoirs for the proliferation of various pathogenic microorganisms. Numerous molecular techniques have been documented in scientific literature to identify bacterial species inside environmental samples10,11,12,13.

Numerous scientific investigations have been conducted to delve deeper into the antibacterial properties of nanoparticles, revealing a multitude of mechanisms by which they effectively inhibit the growth and survival of microbes. Metal nanoparticles, including silver, gold, zinc and magnesium, have been found to exhibit potent antibacterial capabilities. In addition to metal nanoparticles, it has been documented that metal oxide nanoparticles exhibit antibacterial properties14. Capitalizing on metallic nanoparticles is a promising approach to combat these bacterial strains, encompassing both gram-positive and gram-negative classifications. Inorganic antibacterial compounds have recently been employed to control organisms in various industries15,16. Inorganic metal oxide bulk materials are reduced to the nanoscale, which changes their activity and improves their physical, chemical, and biological characteristics17,18. Highly reactive metal oxide nanoparticles have effectively killed gram-positive and gram-negative bacteria.

Nanoscale metal oxide semiconductors are the most spectacular, well-known, and in-demand materials in various fields due to their size, shape, reactivity, and optical and electrical properties. These nanomaterials’ piezo electronic, optoelectronic, and catalytic capabilities make them suitable for solar cells, biosensors, light-emitting diodes, transistors, and light-emitting diodes19,20. The degradation of organic compounds is one of these applications where heterogeneous photocatalysis excels and triumphs. Due to its biocompatibility and excellent photostability, ZnO is an excellent photocatalyst prospect21. Its outstanding physical and chemical qualities, such as its high chemical stability, electrochemical coupling coefficient, and broad light absorption range, make it a material with many uses. It is an innovative and versatile n-type semiconducting material, and its electrons can act as charge carriers to transition from the valence band to the conduction band. A direct large band gap of ZnO is to be 3.37 eV22. Considering where Zn and O are on the periodic table, it is sometimes called an II–VI semiconductor. There is considerable interest in using nanoparticles made of metals and their oxides. Zinc (Zn) and its oxide are among the well-researched metals that impact living items (ZnO). Owing to its powerful reduction characteristics, zinc is an active element. Zinc oxide may be produced readily by oxidation. ZnO is an inorganic semiconductor material with three distinct crystal structures—wurtzite, zinc blende, and rock salt23,24. The structure of wurtzite, in which each zinc atom is tetrahedrally coupled with four oxygen atoms, is thermodynamically stable under ambient circumstances. Furthermore, ZnO nanoparticles offer several benefits, including action against different bacteria, and play an important role in cleaning polluted industrial water using a low dose of nanoparticles.

In line with the above discussion, the present investigation employs co-precipitation to synthesize zinc oxide nanoparticles (PVP-ZnO NPs). The synthesized PVP-ZnO NPs are subsequently employed for photocatalytic and antimicrobial purposes. This exploration of PVP-ZnO NPs imparts a novel understanding of the interrelationship between their inherent properties and potential applications. Despite numerous studies on the synthesis and utilization of zinc oxide nanoparticles (PVP-ZnO NPs) as photocatalysts and antimicrobial agents, the present investigation delves into the evaluation of the underlying mechanisms of reactive oxygen species (ROS) and 2,2-diphenyl-1-picrylhydrazyl (DPPH) assays. This approach contributes an extensive and comprehensive analysis, providing a more profound understanding of the subject matter.

The specific chemicals utilized, namely Polyvinylpyrrolidone (C6H9NO)n, Zinc Nitrate Hexahydrate, and Sodium Hydroxide (NaOH), were acquired from Sigma-Aldrich, Germany. De-ionized (DI) water was consistently employed throughout the experimental process.

In this study, 0.64 g of zinc nitrate was thoroughly dissolved in 25 mL of deionized water and then continuously agitated for 15 min at room temperature at 200 revolutions per minute (rpm). Polyvinylpyrrolidone (PVP) solution was prepared individually using 10 mL DI water and agitated at ambient conditions. The zinc solution was then added gradually to the prepared PVP solution, and the reaction mixture was kept at 70 °C for 2–3 h while stirred at 350 rpm. Meanwhile, NaOH solutionaq. (2.05 g in 40 mL DI) was added dropwise to the resulting liquid to maintain a pH of 9.1. Addition of base to the reaction mixture results in the formation of milky white precipitates. After two to three hours of heating and stirring, the solution was left at room temperature to cool and let the sediments settle. The solution was centrifugated at a speed of 5000 rpm for 4 min, facilitating the collection of precipitates in a centrifuge tube. Subsequently, the precipitates were washed with DI water to eliminate undesired elements. Finally, the gathered precipitates were placed and dried in a hot oven for 24 h at 60 °C. The acquired white color powder was ground into a fine powder in mortar and pestle to create PVP-ZnO NPs. This paper discusses a low-temperature, low-cost, and high-yield (> 85%) method for synthesizing ZnO nanostructures25,26.

The crystallographic properties of the synthesized PVP-PVP-ZnO NPs were characterized using a Panalytical X'PERT PRO X-ray diffractometer (XRD) from the Netherlands, employing Cu Kα (1.5406 Å) monochromatic radiation. The Shimadzu-1800 UV–Vis spectrophotometer was used to measure the absorption spectra over the wavelength range of 200–800 nm. The chemical bonding of the materials was determined by analyzing the transmittance spectra between 4000 and 600 cm−1 through a Bruker FT-IR Spectrometer. Germany-based Carl Zeiss Model Supra 55 The surface morphological properties of the NPs were examined using field emission scanning electron microscopy (FESEM) in conjunction with EDX for elemental content percentages. PHI 5000 VersaProbe III by Physical Electronics was used to measure XPS data. The morphological, physical characteristics and grain size of the NPs were investigated using a Thermo Fisher TALOS F200 S High-Resolution Transmission Electron Microscope (HRTEM) working at 200 kV. The particles were dispersed in ethanol via ultrasonic treatment to facilitate the sample preparation. Subsequently, the resulting suspension was deposited onto a carbon-coated copper grid and dried before capturing the HRTEM images.

Two strains, Escherichia coli (ATCC25922) and Bacillus subtilis (DSM6633), were employed to assess the antibacterial effectiveness of the synthesized samples. These bacterial strains were sourced from the biotechnology laboratory of Sri Guru Granth Sahib World University. These strains were incubated at 37 °C overnight while sub-culturing on Luria Bertani medium (LB). To evaluate the antibacterial activity, the agar diffusion method was used. The homogeneous inoculation of the LB medium was carried out using a sterile swab of bacterial strain (Luria–Bertani). Subsequently, LB-agar plates were punctured with 3–4 wells to accommodate the prepared samples, available in four different concentrations: 100 μg/mL, 600 μg/mL, 1 mg/mL, and 3 mg/mL. Following incubation at 37 °C for 24 h, the diameter of the inhibitory zones surrounding the wells was measured. The zone of inhibition was measured from the well's centre outward to the point where bacterial growth first appeared. For various concentrations, distilled water was used to dissolve each sample.

The DPPH test assessed the free radical scavenging activity of PVP-ZnO NPs, as previously described in the literature27,28. This activity used 2,2 diphenyl-1-picrylhydrazyl, free radical DPPH, and methanol. The DPPH solution was made in the dark using magnetic stirring for 30 min. In absolute methanol, a 15 mM concentration of DPPH solution was made. 100 μL of PVP-ZnO NPs with concentrations of 10, 20, 30, and 40 µg/mL were added to 200 µL of DPPH solution for this test. The mixture was briskly agitated and allowed to stand for 1 h. After 1 h, the absorbance at 518 nm was measured to determine the decrease of the DPPH radical. As a positive control, ascorbic acid was used. The RSA was calculated by using the equation:

where A0 and A are the absorbances of (DPPH·) in solutions.

The experiments were performed three times. Mean ± Standard Deviation (SD) is used to represent the values. The Origin 9.0 software computed the ZnO inhibition value.

The degradation rate of reactive red 141 was used to evaluate the photocatalytic activities of nanoparticles under solar light. In a working experiment, 5 mg/L of RR 141 solution was mixed with 20 mg/L of catalyst (PVP-ZnO NPs) with constant stirring. Then, sunlight was used to illuminate the solution. Approximately 5 mL of sample was collected after photo-irradiation, centrifuged to obtain the supernatant, and then analyzed using the UV–Vis spectrophotometer.

X-ray diffraction (XRD) analysis determines the unit cell’s phase composition and lattice spacings (d-values) in the crystalline material. This information is crucial for determining the crystal structure and crystallite size of the synthesized PVP-ZnO NPs. A crystalline material’s X-ray diffraction (XRD) pattern represents a unique fingerprint characterized by multiple diffraction peaks with varying intensities. This collected XRD data is then compared to readily available reference databases to identify the phases present in the material.

Figure 1 depicted the XRD pattern of PVP-ZnO NPs and the peaks at 2θ = 31.2268°, 34.5679°, 36.2348°, 46.5897°, 57.5491°, 61.9624°, 65.5796°, 67.6246°, and 69.9730° correspond to (100), (002), (101), (102), (110), (103), (200), (112), (201) diffraction planes, respectively as shown in Table 1. All diffraction peaks can be indexed by the hexagonal wurtzite-type structure, which is in accordance with JCPDS No. 00-036-145129. The crystalline parameters of the unit cell provided by XRD and the XRD pattern matched with standard JCPDS data confirm its wurtzite hexagonal structure. An outstanding planar similarity was attained when measured against the generated PVP-ZnO NPs. By excluding any other reflections in the pattern that are either not ZnO or associated with contaminants, it is shown that the spherical shape particles are pure wurtzite hexagonal phase ZnO. The peaks were evidence of the consistent hexagonal structure of wurtzite. From the data, particle size was calculated using the Debye Scherrer equation, which was around 22.13 nm. The crystal size is determined from the above data using Scherrer Debye’s Eq. (1)30.

where k = 0.95–0.98 (shape factor), λ = 0.154 nm (X-ray wavelength), β = half width of the diffraction band FWHM (radians), θ = Bragg’s diffraction angle.

(a) XRD spectrum of Chemical synthesized ZnO Nanoparticles along with JCPDS ruler (inset), (b) Williamson–Hall plot, and (c) modified Scherrer’s Equation.

The calculated size by using Scherrer’s equation is = 22.13 nm.

where β = Total broadening, θ = Bragg’s angle, k = 0.95–0.98 (shape factor), λ = 0.154 nm (X-Ray wavelength).

The calculated size by using the Williamson-Hall equation is = 28.61 nm, as shown in Table 2.

where ln = taking log on both sides, k = 0.95–0.98 (shape factor), λ = 0.154 nm (X-ray wavelength) β = half width of the diffraction band FWHM (radians), θ = Bragg’s diffraction angle.

Using a modified form of Scherrer’s equation, the size is calculated to be = 21.87 nm, as depicted in Table 3.

At room temperature, UV–Vis spectroscopy was used to examine the optical properties of the freshly manufactured spherical-shaped ZnO nanomaterial. The results are shown in Fig. 2a. For UV–Vis measurements, ZnO spheres (powder form) are well-dispersed in water, and the solution of dispersed ZnO water was used to track absorption over the wavelength range of 200–800 nm. As can be seen, the resulting UV–Vis spectrum has a prominent excitonic absorption peak at 367 nm, which corresponds to bulk ZnO in the hexagonal phase of wurtzite. The excitonic absorption peak at 367 nm is the only peak seen in the spectrum, demonstrating the ZnO nanostructures’ purity and exceptional optical properties.

(a) UV–Vis spectrum, (b) Tauc’s plot of chemically synthesized PVP-ZnO NPs.

A Tauc’s plot of the UV–Visible spectrum was plotted, and the related energy bandgap was identified in Fig. 2b. According to this spectrum, direct Eg transitions in synthetic ZnO Nano spherical should have an energy of roughly 3.36 eV, nearly equal to bulk zinc oxide. Using Eq. (2), the direct band gap energy was calculated31,32.

where h = Planck’s constant, \(\nu \) = frequency of vibration, \(\alpha \) = absorption coefficient, Eg = band gap, A = proportional constant.

In Fig. 3, FTIR analysis of PVP-ZnO NPs is shown. The transmittance band at 697 cm−1 for PVP-ZnO NPs may be attributed to Zn–O stretching, proving that the PVP-ZnO NPs are positively generated. The presence of water adsorption on the surface of the nanoparticles is evident from the observed bands at 3717 cm−1, which correspond to the stretching vibrations of the hydroxyl (O–H) groups. The band observed at 2341 cm−1 can be attributed to CO2 in the ambient air. Additionally, the stretching vibration of the C=O bond is observed at 948 cm-1, and the C–H vibration mode is shown on the band at 1725 cm−133,34. Table 4 shows the FTIR spectra peaks.

FTIR spectrum of chemical synthesized PVP-ZnO NPs.

The chemically prepared PVP–PVP-ZnO NPs morphology was further examined using field emission scanning electron microscopy (FESEM). The analysis confirmed that the NPs have a spherical morphology, as shown in Fig. 4. Additionally, the FESEM images revealed that the particles are ordered into nanostructures and tend to clump together. The agglomeration of NPs is caused by the feeble adhesion of particles to one another, resulting in (sub)micron-sized entities. In contrast, NPs aggregates result from forming covalent or metallic bonds that are difficult to break. The spherical form of the NPs can be easily observed. The low magnification FESEM pictures are shown in Fig. 4a at 20 μm, and high magnification images of the products are shown in Fig. 4b at 1 μm35,36.

FESEM images of chemically obtained PVP-ZnO NPs (a) low magnification at 1 μm, (b) high magnification at 200 nm.

The composition of PVP-ZnO NPs is investigated using Energy Dispersive Spectroscopy (EDS), as shown in Fig. 5. According to the EDS analysis, the synthetic compounds are made of zinc (Zn) and oxygen (O). No further peaks in the EDS spectrum connected to any contaminant are visible up to the instrument's detection limit. This demonstrates that the synthesized products are pure ZnO made of zinc (Zn) and oxygen (O)37.

Edx spectrum of Chemical synthesized PVP-ZnO NPs.

The HRTEM images of the created zinc oxide nanoparticles are shown in Fig. 6. The size of the produced ZnO-NPs was determined to be varying from 20 to 30 nm, which is in complete agreement with the value obtained from the XRD data, and the HRTEM images show that they are polycrystalline with a spherical structure. The higher-resolution HRTEM images also show that NPs are separated by a uniform interparticle distance rather than being in direct touch. The high-resolution transmission electron microscopy (HRTEM) image (Fig. 6b) provides clear evidence of the presence of the “002” plane in the wurtzite crystal structure of ZnO. The observed pattern consists of well-resolved and continuous fringes, with a measured lattice spacing of 2.83, confirming the characteristic arrangement of atoms within the ZnO crystal lattice.

HRTEM images of PVP-ZnO NPs at different scale bars with size distribution histogram and lattice fringes (inset).

XPS was used to analyze the elemental composition of ZnO nanoparticles and their states on the surface. As seen in Fig. 7, all of the peaks belong to the elements zinc and oxygen, which is consistent with the findings of the EDS. The binding energy peaks of Zn 2p1/2 and Zn 2p3/2 are found at 1033.6 and 1010.02 eV, respectively, in the Zn 2p spectrum (Fig. 7a). The fact that there is a difference of 23.58 eV in energy between the two peaks indicates that the valence state of the Zn element is + 2 and that it exists in the form of ZnO. According to the findings from the O 1s spectra (shown in Fig. 4b), the binding energy peak of the O 1s molecule displays symmetry, with 531.87 eV dissolving into a lattice ion. It has been demonstrated that ionic substitution occurs, producing oxygen substitution inside the lattice. The C1s are depicted in Fig. 7c. The BE distance between the two peaks in the C1s XPS spectrum of ZnO is 4.1 eV. The ZnO C1s XPS spectrum’s primary peak is 284.9 eV, and the satellite peak is 288.1 eV. The peak at 284.6 eV is ascribed to carbon contamination. The peak at 285.7 eV is associated with the C–O band. The peak at 288.8 eV is caused by surface carbonate species that are loosely bound, such as C=O, and carbon may be incorporated into the interstitial positions of the ZnO lattice.

X-ray photoelectron images of synthesized PVP-ZnO NPs (a) Zn (2p3/2, 2p1/2), (b) O-1s state, and (c) C1s state.

To investigate the charge transfer and migration properties of PVP-ZnO NPs, the photoluminescence spectra (PL) were obtained. The PL emission intensity results from recombining photoexcited electron-/hole pairs; consequently, lower and higher PL emission intensities indicate lower and greater recombination of photogenerated charge carriers, respectively. The PL emission spectra of all synthesized photocatalysts are shown in Fig. 8. The obtained spectra can be divided into two distinct regions, one known as the band edge emission region, with a wavelength range of 375 to 395 nm. The recombination of conduction band electrons and valence band holes causes this first region of the emission spectrum. The second emission region in the wavelength range of 525 to 575 nm may be attributed to the defects emission region, where defects in the ZnO structure cause emission.

Photoluminescence emission spectra of ZnO.

In the present research, the NPs diffusion technique was used to investigate whether or not PVP-ZnO NPs are effective against E. coli and B. subtilis. E. coli is a gram-negative bacterium, and B. subtilis is a gram-positive bacterium. This test covered both types of bacteria, which are representative of other bacterial strains basis on this feature. Also, according to the Centres for disease control and Prevention, E. coli is found in the environment, food, and untreated water. Hence, evaluation against it also means we can tackle other bacteria dwelling in the same sources. Because of their reduced toxicity, zinc oxide nanoparticles (PVP-ZnO NPs) were the subject of research to see whether or not they were useful as a possible raw material for various biological applications, most notably as an antibacterial agent.

Figure 9 depicts the dose-dependent enhancement of antibacterial activity, establishing a correlation between the increased concentration of ZnO nanoparticles (NPs) and improved activity. Our study findings reveal the potent antibacterial impact of PVP-ZnO NPs on E. coli, whereas their antibacterial effect on B. subtilis is comparatively modest. The disparity in growth inhibition between the two bacterial types can be attributed to the structural differences in their cell walls. E. coli, a gram-negative bacterium with a thin cell wall, is more susceptible to the antibacterial properties of PVP-ZnO NPs, whereas B. subtilis, a gram-positive bacterium with a thick cell wall, exhibits reduced sensitivity. In negative control, checked against water, zinc nitrate and PVP, no zone of inhibition is observed; in positive control, a clear zone of inhibition (25 mm) is observed. PVP-ZnO NPs were given to the subjects at 100 μg/mL, 600 μg/mL, 1 mg/mL, and 3 mg/mL, respectively. PVP-ZnO NPs had a maximal zone of inhibition of 20 mm ± 0.15 mm for B. subtilisand 24 mm ± 0.19 mm, for E. coli. Consequently, the larger surface area of ZnO nanoparticles is attributed to their increased antibacterial activity (Fig. 10).

Agar plates with PVP-ZnO NPs that have zones of inhibition against bacteria (a) negative control, (b) positive control, (c) E. coli, and (d) B. subtilis.

Histogram shows the zone of clearance by PVP-ZnO NPs.

PVP-ZnO NPs were specifically examined for their potential application as an antibacterial agent owing to their comparatively lower toxicity. The enhanced antibacterial effectiveness of PVP-ZnO NPs can be attributed to their increased surface area, oxygen vacancies, release of Zn2+ ions, and ability to disperse as reactive molecules. The increased specific surface area to volume ratio and reduced crystallite size of PVP-ZnO NPs lead to extra vacancies and reactive oxygen species (ROS) production. PVP-ZnO NPs exhibit antibacterial activity primarily due to the presence of oxygen vacancies influenced by Zn2+ ions. These vacancies generate reactive oxygen species (ROS) like hydrogen peroxide (H2O2), O2−, and OH, which can cause DNA damage and apoptosis38,39. The degree of contact between the nanomaterial and the bacteria cell membrane determines the shape-based antibacterial action. Spherical-shaped NPs have a large surface area exposed that can bind to the bacteria40. Table 5 shows the comparison detail of antibacterial study performance.

The electrostatic interaction between positively charged Zn2+ ions from ZnO nanoparticles (NPs) and the negatively charged bacterial cell membrane results in transmembrane pores and disrupting membrane permeability. This is a feasible antibacterial activity of PVP-ZnO NPs, as seen in Fig. 11.

Mechanism of antibacterial.

Free radical scavenging activity of synthesised PVP-ZnO NPs may be quickly and easily estimated using DPPH. PVP-ZnO NPs cause a drop in absorbance at 517 nm, confirming the color change from purple to yellow. By donating electrons from the oxygen atoms to the odd electrons of the nitrogen atoms, DPPH is converted into DPPH free radicals, and the molecule DPPH is formed. Surface oxidation–reduction processes occur when ZnO nanostructures are stimulated at the right wavelength, generating holes. ZnO, a semiconductor, was a trap for the electrons, interacting with oxygen and water to produce HO2. Organic dyes degraded because hydroxyl surface groups blocked the holes, releasing OH radicals. The antioxidant activity of ZnO NP’s was found in Fig. 12 to increase with the increase in concentration from 10 to 40 µg/mL.

DPPH scavanging ability of PVP-ZnO NPs.

One of the most important uses of eco-friendly photocatalysts is the photodegradation of organic dye, namely reactive red-141 azo dye from the textile industry. To comprehend the possible uses of ZnO nanostructures created using a prepared PVP capping agent. The photocatalytic performance of a ZnO sample was evaluated by monitoring the degradation of reactive red (RR-141) dye (initial concentration: 5 mg/L) under direct solar light exposure over a defined duration. Absorption spectra of RR-141 dye solution with PVP-ZnO NPs for up to 120 min are depicted in Fig. 13a,c, respectively. Under the influence of solar light and in the presence of ZnO photocatalyst, the RR-141 azo dye’s highest absorption peak at 546 nm steadily reduced during the experiment as time passed, as shown in Fig. 13b,c. After 120 min, the absorption peak of RR-141 azo dye at 546 nm completely disappeared. This demonstrates the photocatalytic dye degradation potency of obtained PVP-ZnO NPs (88% with 10 mg catalyst and nearly 95% with 20 mg catalyst), as shown in Fig. 13d. Different shapes and sizes of nanoparticles influence the rate of photocatalysis as it changes the proportion of exposed polar faces. Because of the positive charge and more proportion of the ZnO facet, OH− ions could preferentially adsorb on this face. This would result in a faster rate of formation of OH radicals and so dye degradation during photocatalysis45.

Shows (a) absorption spectra without photocatalyst, (b) absorption spectra of RR-141 with 10 mg catalyst, (c) absorption spectra of RR-141 with 20 mg catalyst, (d) degradation efficiency, (e) Pseudo-first-order kinetic (10 mg catalyst), and (f) Pseudo first-order kinetic (20 mg catalyst).

The rate of process degradation can serve as a measure for assessing the photocatalytic activity of the obtained PVP-ZnO NPs46,47. The modified Langmuir–Hinshelwood (L–H) equations are employed to account for solid–liquid interface reactions, allowing for a rationalized model. This model enables the characterization of steady-state photocatalytic reactions within a heterogeneous photocatalyst system. The pseudo-first-order reaction kinetics of PVP-ZnO NPs for the degradation of RR-141 azo dye has been estimated through the following equation:

where k1 denotes the reaction rate constant for a pseudo-first-order photodegradation, A representation of ln (C0/C) vs. the irradiation duration for the RR-141 degradation catalyzed by each capped ZnO nanostructure is shown in Fig. 13e,f. This shows that pseudo-first-order kinetics governs the photodegradation of the azo dye RR-141 by ZnO photocatalysts. The resulting equation was used to determine the linear fit for each analysis. The slope provides the constant rate of change or k1. A pseudo-first-order kinetic equation governs the photocatalytic degradation reaction of an azo dye, according to the high R2 value (> 0.9).

Figure 14 depicts a schematic representation of the photocatalytic reaction mechanism.

Photocatalytic mechanism.

When the energy of direct sunlight in terms of photons is equal to or greater than the bandgap of ZnO, the electrons receive energy, and electrons are transferred from the valence band to the conduction band, resulting in the formation of a hole (h+) and an electron (e−) in the valence band48,49. The pores react with water to produce. OH radicals, which are capable of oxidizing the organic pollutants50,51.

During the reduction process, the conduction band electron reacts with oxygen to produce.OH radicals. These radicals inhibit the production of organic contaminants. Under direct sunlight irradiation, these oxidation and reduction processes could degrade the organic pollutants. Based on earlier studies53, the following equation explains the photocatalytic reaction mechanism: The detailed summary of photocatalytic degradation of pollutants is shown in Table 6

In this work, PVP-ZnO NPs have been successfully prepared via the co-precipitation method using PVP as a capping agent. The structural morphology, size, and configuration of PVP-ZnO NPs were studied using FTIR, XRD, FESEM, HRTEM, XPS and UV–Visible spectroscopic analysis, which indicates the formation of spherical-shaped ZnO NPs having a size varying from 20 to 30 nm. Further, the synthesized nanoparticles were evaluated for their antibacterial and photocatalytic potential. This study reveals the potent antibacterial impact of PVP-ZnO NPs against E. coli and B. subtilis. The antibacterial effect on E. coli is higher as compared to B. subtilis. This study also demonstrated the photocatalytic dye (reactive red-141) degradation potency of obtained PVP-ZnO NPs and degraded 88% and 95% using 10 mg catalyst and 20 mg catalyst, respectively. ROS species’ generation is the main factor for photocatalytic and antimicrobial studies, which was investigated through DPPH antioxidant assays. Thus, this study explores the effective platform for environmental remediation applications and delves into a way for future researchers to work on the multidisciplinary applications of metal oxide nanoparticles.

The datasets used and analyzed during the current study are available from the corresponding author upon reasonable request.

Adel, M., Ahmed, M. A. & Mohamed, A. A. Effective removal of indigo carmine dye from wastewaters by adsorption onto mesoporous magnesium ferrite nanoparticles. Environ. Nanotechnol. Monit. Manag. 16, 100550 (2021).

CAS Google Scholar

Li, X. L., Zhang, W., Huang, Y. Q., Wang, Q. & Yang, J. M. Superior adsorptive removal of azo dyes from aqueous solution by a Ni(II)-doped metal–organic framework. Colloids Surf. A Physicochem. Eng. Asp. 619, 126549 (2021).

Article CAS Google Scholar

Chankhanittha, T. et al. Silver decorated ZnO photocatalyst for effective removal of reactive red azo dye and ofloxacin antibiotic under solar light irradiation. Colloids Surf. A Physicochem. Eng. Asp. 626, 127034 (2021).

Article CAS Google Scholar

Singh, J., Kaur, N. & Rawat, M. Eco-friendly approach for synthesis of AgNPs and their catalytic application toward 4-nitrophenol to 4-aminophenol reduction. Micro Nano Lett. 13, 1600–1603 (2018).

Article CAS Google Scholar

Yola, M. L., Eren, T., Atar, N. & Wang, S. Adsorptive and photocatalytic removal of reactive dyes by silver nanoparticle-colemanite ore waste. Chem. Eng. J. 242, 333–340 (2013).

Article Google Scholar

Rani, P., Varma, R. S., Singh, K., Acevedo, R. & Singh, J. Catalytic and antimicrobial potential of green synthesized Au and Au@Ag core-shell nanoparticles. Chemosphere 317, 137841 (2023).

Article ADS CAS PubMed Google Scholar

Singh, J., Singh, K., Singh, J. & Rawat, M. Green synthesis of zinc oxide nanoparticles using Punica granatum leaf extract and its application towards photocatalytic degradation of Coomassie brilliant blue R-250 dye. SN Appl. Sci. 1, 1–8. https://doi.org/10.1007/S42452-019-0610-5 (2019).

Article Google Scholar

Chankhanittha, T., Watcharakitti, J. & Nanan, S. PVP-assisted synthesis of rod-like ZnO photocatalyst for photodegradation of reactive red (RR141) and Congo red (CR) azo dyes. J. Mater. Sci. Mater. Electron. 30, 17804–17819 (2019).

Article CAS Google Scholar

Vanaamudan, A., Chavada, B. & Padmaja, P. Adsorption of reactive blue 21 and reactive red 141 from aqueous solutions onto hydrotalcite. J. Environ. Chem. Eng. 4, 2617–2627 (2016).

Article CAS Google Scholar

Serwecińska, L. Antimicrobials and antibiotic-resistant bacteria: A risk to the environment and to public health. Water 12, 3313 (2020).

Article Google Scholar

Singh, K., Singh, G. & Singh, J. Sustainable synthesis of biogenic ZnO NPs for mitigation of emerging pollutants and pathogens. Environ. Res. 219, 114952 (2023).

Article CAS PubMed Google Scholar

Ahmad, N. S., Abdullah, N. & Yasin, F. M. Toxicity assessment of reduced graphene oxide and titanium dioxide nanomaterials on gram-positive and gram-negative bacteria under normal laboratory lighting condition. Toxicol. Rep. 7, 693–699 (2020).

Article CAS PubMed PubMed Central Google Scholar

Osunmakinde, C. O., Selvarajan, R., Mamba, B. B. & Msagati, T. A. M. Profiling bacterial diversity and potential pathogens in wastewater treatment plants using high-throughput sequencing analysis. Microorganisms 7, 506 (2019).

Article CAS Google Scholar

Gharpure, S., Akash, A. & Ankamwar, B. A review on antimicrobial properties of metal nanoparticles. J. Nanosci. Nanotechnol. 20, 3303–3339 (2019).

Article Google Scholar

Ramesh, C., Vinithkumar, N. V. & Kirubagaran, R. Marine pigmented bacteria: A prospective source of antibacterial compounds. J. Nat. Sci. Biol. Med. 10, 104–113 (2019).

Article CAS Google Scholar

Deshmukh, S. K. et al. Fungal endophytes: A potential source of antibacterial compounds. J. Fungi 8, 164 (2022).

Article CAS Google Scholar

Tripathy, N. & Kim, D. H. Metal oxide modified ZnO nanomaterials for biosensor applications. Nano Converg. 5, 1–10 (2018).

Article Google Scholar

Singh, K. et al. ZnO and cobalt decorated ZnO NPs: Synthesis, photocatalysis and antimicrobial applications. Chemosphere 313, 137322 (2023).

Article ADS CAS PubMed Google Scholar

Sabouri, Z., Akbari, A., Hosseini, H. A. & Darroudi, M. Facile green synthesis of NiO nanoparticles and investigation of dye degradation and cytotoxicity effects. J. Mol. Struct. 1173, 931–936 (2018).

Article ADS CAS Google Scholar

Hasnidawani, J. N. et al. Synthesis of ZnO nanostructures using sol-gel method. Procedia Chem. 19, 211–216 (2016).

Article CAS Google Scholar

Goel, S., Sinha, N., Yadav, H., Joseph, A. J. & Kumar, B. Experimental investigation on the structural, dielectric, ferroelectric and piezoelectric properties of La doped ZnO nanoparticles and their application in dye-sensitized solar cells. Phys. E Low Dimens. Syst. Nanostruct. 91, 72–81 (2017).

Article ADS CAS Google Scholar

Davis, K., Yarbrough, R., Froeschle, M., White, J. & Rathnayake, H. Band gap engineered zinc oxide nanostructures: Via a sol-gel synthesis of solvent driven shape-controlled crystal growth. RSC Adv. 9, 14638–14648 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Rahman, W., Garain, S., Sultana, A., Ranjan Middya, T. & Mandal, D. Self-powered piezoelectric nanogenerator based on wurtzite ZnO nanoparticles for energy harvesting application. Mater. Today Proc. 5, 9826–9830 (2018).

Article CAS Google Scholar

Zagal-Padilla, C. K., García-Sandoval, J. & Gamboa, S. A. A feasible and low-cost green route to prepare ZnO with n or p-type conductivity by changing the parsley extract concentration. J. Alloys Compd. 891, 162087 (2022).

Article CAS Google Scholar

Devi, P. G. & Velu, A. S. Synthesis, structural and optical properties of pure ZnO and Co doped ZnO nanoparticles prepared by the co-precipitation method. J. Theor. Appl. Phys. 10, 233–240 (2016).

Article ADS Google Scholar

Ahamed, A. J. & Vijaya Kumar, P. Synthesis and characterization of ZnO nanoparticles by co-precipitation method at room temperature. J. Chem. Pharm. Res. 8, 624–628 (2016).

CAS Google Scholar

Apak, R. et al. Methods to evaluate the scavenging activity of antioxidants toward reactive oxygen and nitrogen species (IUPAC Technical Report). Pure Appl. Chem. 94, 87–144 (2022).

Article CAS Google Scholar

Wu, M. et al. ZnO nanoparticles stabilized oregano essential oil pickering emulsion for functional cellulose nanofibrils packaging films with antimicrobial and antioxidant activity. Int. J. Biol. Macromol. 190, 433–440 (2021).

Article CAS PubMed Google Scholar

Kumar, S., Kaushik, R. D. & Purohit, L. P. ZnO–CdO nanocomposites incorporated with graphene oxide nanosheets for efficient photocatalytic degradation of bisphenol A, thymol blue and ciprofloxacin. J. Hazard. Mater. 424, 127332 (2022).

Article CAS Google Scholar

Ozugurlu, E. Cd-doped ZnO nanoparticles: An experimental and first-principles DFT studies. J. Alloys Compd. 861, 158620 (2021).

Article CAS Google Scholar

Roy, S., Ghosh, M. P. & Mukherjee, S. Introducing magnetic properties in Fe-doped ZnO nanoparticles. Appl. Phys. A 127, 1–9 (2021).

Article Google Scholar

Mohamed Riyas, Z., Gayathri, R., Prabhu, M. R., Velsankar, K. & Sudhahar, S. Green synthesis and biomedical behavior of Mg-doped ZnO nanoparticle using leaf extract of Ficus religiosa. Ceram. Int. 48, 24619–24628 (2022).

Article CAS Google Scholar

Gabrienko, A. A. et al. Isobutene transformation to aromatics on Zn-modified zeolite: Particular effects of Zn2+ and ZnO species on the reaction occurrence revealed with solid-state NMR and FTIR spectroscopy. J. Phys. Chem. C 125, 15343–15353 (2021).

Article CAS Google Scholar

Alanazi, H. S., Ahmad, N. & Alharthi, F. A. Synthesis of Gd/N co-doped ZnO for enhanced UV–Vis and direct solar-light-driven photocatalytic degradation. RSC Adv. 11, 10194–10202 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Joshi, N. C. & Kumar, N. Synthesis, characterisation and adsorption applications of PMMA/ZnO-based nanocomposite material. Nanotechnol. Environ. Eng. 7, 425–436 (2022).

Article CAS Google Scholar

Lam, S.-M. et al. Ameliorated photodegradation performance of polyethylene and polystyrene films incorporated with ZnO-PVP catalyst. J. Environ. Chem. Eng. 10, 107594 (2022).

Article CAS Google Scholar

Achehboune, M. et al. Microstructural, FTIR and Raman spectroscopic study of rare earth doped ZnO nanostructures. Mater. Today Proc. 53, 319–323 (2021).

Article Google Scholar

Rahmah, M. I. & Qasim, H. B. A novel method to prepare antibacterial ZnO nanoflowers. Appl. Phys. A Mater. Sci. Process. 128, 998 (2022).

Article ADS CAS Google Scholar

Rahmah, M. I., Sabry, R. S. & Aziz, W. J. Preparation and antibacterial activity of superhydrophobic modified ZnO/PVC nanocomposite. J. Bionic Eng. 19, 139–154 (2022).

Article Google Scholar

Menichetti, A., Mavridi-Printezi, A., Mordini, D. & Montalti, M. Effect of size, shape and surface functionalization on the antibacterial activity of silver nanoparticles. J. Funct. Biomater. 14, 244 (2023).

Article CAS PubMed PubMed Central Google Scholar

Zhao, Y., Ma, J., Liu, J. & Bao, Y. Synthesis of fireworks-shaped ZnO/graphite-like carbon nanowires with enhanced visible-light photocatalytic activity and anti-photocorrosion. Colloids Surf. A Physicochem. Eng. Asp. 518, 57–63 (2017).

Article CAS Google Scholar

Karthik, K., Dhanuskodi, S., Gobinath, C. & Sivaramakrishnan, S. Microwave-assisted synthesis of CdO-ZnO nanocomposite and its antibacterial activity against human pathogens. Spectrochim. Acta A Mol. Biomol. Spectrosc. 139, 7–12 (2015).

Article ADS CAS PubMed Google Scholar

Zirak, M., Akhavan, O., Moradlou, O., Nien, Y. T. & Moshfegh, A. Z. Vertically aligned ZnO@CdS nanorod heterostructures for visible light photoinactivation of bacteria. J. Alloys Compd. 590, 507–513 (2014).

Article CAS Google Scholar

Yalcinkaya, F. & Lubasova, D. Quantitative evaluation of antibacterial activities of nanoparticles (ZnO, TiO2, ZnO/TiO2, SnO2, CuO, ZrO2, and AgNO3) incorporated into polyvinyl butyral nanofibers. Polym. Adv. Technol. 28, 137–140 (2017).

Article CAS Google Scholar

Mclaren, A., Valdes-Solis, T., Li, G. & Tsang, S. C. Shape and size effects of ZnO nanocrystals on photocatalytic activity. J. Am. Chem. Soc. 131, 12540–12541 (2009).

Article CAS PubMed Google Scholar

Thakur, N., Thakur, N., Kumar, K. & Kumar, A. Tinospora cordifolia mediated eco-friendly synthesis of cobalt doped TiO2 NPs for degradation of organic methylene blue dye. Mater. Today Proc. https://doi.org/10.1016/j.matpr.2023.01.253 (2023).

Article Google Scholar

Thakur, N., Thakur, N. & Kumar, K. Phytochemically and PVP stabilized TiO2 nanospheres for enhanced photocatalytic and antioxidant efficiency. Mater. Today Commun. 35, 105587 (2023).

Article CAS Google Scholar

Rahmah, M. I., Sabry, R. S. & Aziz, W. J. Synthesis and study photocatalytic activity of Fe2O3-doped ZnO nanostructure under visible light irradiation. Int. J. Environ. Anal. Chem. 101, 2598–2611 (2021).

Article CAS Google Scholar

Sabry, R. S., Aziz, W. J. & Rahmah, M. I. Employed silver doping to improved photocatalytic properties of ZnO micro/nanostructures. J. Inorg. Organomet. Polym. Mater. 30, 4533–4543 (2020).

Article CAS Google Scholar

Kumar, P., Thakur, N., Kumar, K. & Jeet, K. Photodegradation of methyl orange dye by using Azadirachta indica and chemically mediated synthesized cobalt doped α-Fe2O3 NPs through co-precipitation method. Mater. Today Proc. https://doi.org/10.1016/j.matpr.2023.01.257 (2023).

Article PubMed Google Scholar

Zewde, D. & Geremew, B. Biosynthesis of ZnO nanoparticles using Hagenia abyssinica leaf extracts; their photocatalytic and antibacterial activities. Environ. Pollut. Bioavailab. 34, 224–235 (2022).

Article CAS Google Scholar

Aftab, S. et al. Highly efficient visible light active doped ZnO photocatalysts for the treatment of wastewater contaminated with dyes and pathogens of emerging concern. Nanomaterials 12, 486 (2022).

Article CAS PubMed PubMed Central Google Scholar

Yadav, A., Kumar, H., Sharma, R., Kumari, R. & Thakur, M. Quantum dot decorated polyaniline plastic as a multifunctional nanocomposite: Experimental and theoretical approach. RSC Adv. 12, 24063–24076 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Rohilla, S. et al. Excellent UV-light triggered photocatalytic performance of ZnO⋅Sio2 nanocomposite for water pollutant compound methyl orange dye. Nanomaterials 11, 2548 (2021).

Article CAS PubMed PubMed Central Google Scholar

Ebrahimi, R. et al. Effects of doping zinc oxide nanoparticles with transition metals (Ag, Cu, Mn) on photocatalytic degradation of Direct Blue 15 dye under UV and visible light irradiation. J. Environ. Health Sci. Eng. 17, 479–492 (2019).

Article CAS PubMed PubMed Central Google Scholar

Devi, S. A., Singh, K. J. & Devi, K. N. A comparative study on the photocatalytic activity of eucalyptus leaf assisted green synthesized ZnO and chemically synthesized ZnO towards the degradation of malachite green dye. Integr. Ferroelectr. 205, 38–51 (2020).

Article ADS CAS Google Scholar

Ahmad, M. et al. Phytogenic fabrication of ZnO and gold decorated ZnO nanoparticles for photocatalytic degradation of Rhodamine B. J. Environ. Chem. Eng. 9, 104725 (2021).

Article CAS Google Scholar

Wannakan, K., Khansamrit, K., Senasu, T. & Nanan, S. Ultrasound-assisted synthesis of a ZnO/BiVO4 S-scheme heterojunction photocatalyst for degradation of the reactive red 141 dye and oxytetracycline antibiotic. ACS Omega 8, 4835–4852 (2023).

Article CAS PubMed PubMed Central Google Scholar

Kakarndee, S. & Nanan, S. SDS capped and PVA capped ZnO nanostructures with high photocatalytic performance toward photodegradation of reactive red (RR141) azo dye. J. Environ. Chem. Eng. 6, 74–94 (2018).

Article CAS Google Scholar

Chankhanittha, T. et al. ZnO/ZnS photocatalyst from thermal treatment of ZnS: Influence of calcination temperature on development of heterojunction structure and photocatalytic performance. J. Phys. Chem. Solids 179, 111393 (2023).

Article CAS Google Scholar

Saravanan, R., Gupta, V. K., Narayanan, V. & Stephen, A. Comparative study on photocatalytic activity of ZnO prepared by different methods. J. Mol. Liq. 181, 133–141 (2013).

Article CAS Google Scholar

Download references

The authors gratefully acknowledge Sri Guru Granth Sahib World University, Fatehgarh Sahib, Punjab, and Chandigarh University Mohali, Punjab, (India) for research lab facilities.

Department of Electronics Engineering, Sri Guru Granth Sahib World University, Fatehgarh Sahib, Punjab, 140406, India

Karanpal Singh & Gurjinder Singh

Department of Biotechnology, Sri Guru Granth Sahib World University, Fatehgarh Sahib, Punjab, 140406, India

Nancy

Department of Chemistry, University Centre for Research and Development, Chandigarh University, Gharuan, Mohali, 140413, India

Monika Bhattu & Jagpreet Singh

Department of Electrical and Electronics & Communication Engineering, DIT University, Dehradun, Uttarakhand, 248009, India

Gurjinder Singh

Petroleum and Chemical Engineering, Faculty of Engineering, Universiti Teknologi Brunei, Bandar Seri Begawan, BE1410, Brunei Darussalam

Nabisab Mujawar Mubarak

Department of Biosciences, Saveetha School of Engineering, Saveetha Institute of Medical and Technical Sciences, Chennai, India

Nabisab Mujawar Mubarak

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

K.S.: Data curation, Writing—original draft, Visualization. N.N.: Data curation, Writing—original draft. M.B.: Writing—review & editing, Data curation, Visualization; G.S.: Conceptualization, Formal analysis, Investigation, Data curation; N.M.M.: Conceptualization, Formal analysis, Investigation, Data curation, Writing—review & editing, Visualization. J.S.: Conceptualization, Formal analysis, Investigation, Data curation, Writing—review & editing, Visualization.

Correspondence to Gurjinder Singh, Nabisab Mujawar Mubarak or Jagpreet Singh.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Singh, K., Nancy, Bhattu, M. et al. Light-absorption-driven photocatalysis and antimicrobial potential of PVP-capped zinc oxide nanoparticles. Sci Rep 13, 13886 (2023). https://doi.org/10.1038/s41598-023-41103-7

Download citation

Received: 03 May 2023

Accepted: 22 August 2023

Published: 24 August 2023

DOI: https://doi.org/10.1038/s41598-023-41103-7

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.